van Duijn, J. | bioRxiv Science

bioRxiv2023

3D printed magneto-active microfiber scaffolds for remote stimulation of 3D in vitro skeletal muscle models

Tunable culture platforms that guide cellular organization and mechanically stimulate skeletal muscle development are still unavailable due to limitations in biocompatibility and actuation triggered without contact. This study reports the rational design and fabrication of magneto-active microfiber meshes with controlled hexagonal microstructures via melt electrowriting (MEW) of a thermoplastic/graphene/iron oxide composite. In situ deposition of iron oxide nanoparticles on oxidized graphene yielded homogeneously dispersed magnetic particles with sizes above 0.5 m and low aspect ratio, preventing cellular internalization and toxicity. With these fillers, homogeneous magnetic composites with very high magnetic filler content (up to 10 wt.%) were obtained and successfully processed in a solvent-free manner for the first time. MEW of magnetic composites enabled the skeletal muscle-inspired design of hexagonal scaffolds with tunable fiber diameter, reconfigurable modularity, and zonal distribution of magneto-active and nonactive material. Importantly, the hexagonal microstructures displayed elastic deformability under tension, mitigating the mechanical limitations due to high filler content. External magnetic fields below 300 mT were sufficient to trigger out-of-plane reversible deformation leading to effective end-to-end length decrease up to 17%. Moreover, C2C12 myoblast culture on 3D Matrigel/collagen/MEW scaffolds showed that the presence of magnetic particles in the scaffolds did not significantly affect viability after 8 days with respect to scaffolds without magnetic filler. Importantly, in vitro culture demonstrated that myoblasts underwent differentiation at similar rates regardless of the presence of magnetic filler. Overall, these innovative microfiber scaffolds were proven as a magnetically deformable platform suitable for dynamic culture of skeletal muscle with potential for in vitro disease modeling.

bioengineering↗

bioRxiv2020

Topographic Guidance in Melt-Electrowritten Tubular Scaffolds Enhances Engineered Kidney Tubule Performance

To advance the engineering of kidney tubules for future implantation, constructs should be both self-supportive and yet small-sized and highly porous. Here, we hypothesize that the fabrication of small-sized porous tubular scaffolds with a highly organized fibrous microstructure by means of melt-electrowriting (MEW) allows the development of self-supported kidney proximal tubules with enhanced properties. A custom-built MEW device was used to fabricate tubular fibrous scaffolds with small diameter sizes (O = 0.5, 1, 3 mm) and well-defined, porous microarchitectures (rhombus, square, and random). Human umbilical vein endothelial cells (HUVEC) and human conditionally immortalized proximal tubular epithelial cells (ciPTEC) were seeded into the scaffolds and tested for monolayer formation, integrity, and organization, as well as for extracellular matrix (ECM) production and renal transport functionality. Tubular scaffolds were successfully manufactured by fine control of MEW instrument parameters. A minimum inner diameter of 0.5 mm and pore sizes of 0.2 mm were achieved. CiPTEC formed tight monolayers in all scaffold microarchitectures tested, but well-defined rhombus-shaped pores outperformed and facilitated unidirectional cell orientation, increased collagen type IV deposition, and expression of the renal transporters and differentiation markers organic cation transporter 2 (OCT2) and P-glycoprotein (P-gp). To conclude, we present smaller diameter engineered kidney tubules with microgeometry-directed cell functionality. Due to the well-organized tubular fiber scaffold microstructure, the tubes are mechanically self-supported, and the self-produced ECM constitutes the only barrier between the inner and outer compartment, facilitating rapid and active solute transport.

bioengineering↗