Campbell, K. T. | bioRxiv Science

bioRxiv2020

Evaluation of Alginate-Based Bioinks for 3D Bioprinting, Mesenchymal Stromal Cell Osteogenesis, and Application for Patient-Specific Bone Grafts

To realize the promise of 3D bioprinting, it is imperative to develop bioinks that possess the biological and rheological characteristics needed for the printing of cell-laden tissue grafts. Alginate is widely used as a bioink because its rheological properties can be modified through pre-crosslinking or the addition of thickening agents to increase printing resolution. However, modification of alginates physicochemical characteristics using common crosslinking agents can affect its cytocompatibility. Therefore, we evaluated the printability, physicochemical properties, and osteogenic potential of four common alginate bioinks: alginate-CaCl2 (alg-CaCl2), alginate-CaSO4 (alg-CaSO4), alginate-gelatin (alg-gel) and alginate-nanocellulose (alg-ncel) for the 3D bioprinting of patient-specific osteogenic grafts. While all bioinks possessed similar viscosity, printing fidelity was lower in the pre-crosslinked bioinks. When used to print geometrically defined constructs, alg-CaSO4 and alg-ncel exhibited higher mechanical properties and lower mesh size than those printed with alg-CaCl2 or alg-gel. The physical properties of these constructs affected the biological performance of encapsulated bone marrow-derived mesenchymal stromal cells (MSCs). Cell-laden constructs printed using alg-CaSO4 and alg-ncel exhibited greater cell apoptosis and contained fewer living cells 7 days post-printing. In addition, effective cell-matrix interactions were only observed in alg-CaCl2 printed constructs. When cultured in osteogenic media, MSCs in alg-CaCl2 constructs exhibited increased osteogenic differentiation compared to the other three bioinks. This bioink was then used to 3D print anatomically accurate cell-laden scaphoid bones that were capable of partial mineralization after 14 days of in vitro culture. These results highlight the importance of bioink properties to modulate cell behavior and the biofabrication of clinically relevant bone tissues.

bioengineering↗

bioRxiv2019

Open-source 3D printed air-jet for generating monodispersed alginate microhydrogels

Open-source designs represent an attractive and new tool for research as it provides both affordable and accessible options to the lab environment. In particular, with the advent of new and cheap additive manufacturing technologies, the open-source design of lab hardware enables others to perform research that would be difficult otherwise. This manuscript describes an air-jet system designed to be open-source and simple to produce with 3D printing. The fully 3D printed air-jet was designed for the generation of hydrogel microbeads of a controllable size. Alginate microbeads were used as a working model, given that it has many promising research applications due to their injectability and highly reproducible properties. A fit definitive design of experiments was performed to determine critical factors affecting diameter, index of dispersity, and circularity of microbeads from this air-jet design. By regulating alginate concentration, air pressure, pump speed, and needle diameter could achieve control over microbeads size from 200-800 {micro}m with low variance. Furthermore, we also demonstrate the potential probiotic research applications of the open-source air-jet through the encapsulation of bacteria in alginate microbeads with controllable degradation. The results of this study exhibit an open-source platform for making microscale biomaterials with controllable properties that can be achieved through budget 3D printers.

bioengineering↗